EN 10216-2 Cyfansoddiad Cemegol
|
Gradd dur |
C |
Si |
Mn |
P |
S |
Cr |
Mo |
Ni |
Altot |
Cu |
Ti max |
|
|
Enw dur |
Rhif dur |
max |
max |
|||||||||
|
P195GH |
1.0348 |
=0.13 |
=0.35 |
=0.70 |
0.025 |
0.020 |
=0.30 |
=0.08 |
=0.30 |
=0.020 |
=0.30 |
0.040 |
|
P235GH |
1.0345 |
=0.16 |
=0.35 |
=1.20 |
0.025 |
0.020 |
=0.30 |
=0.08 |
=0.30 |
=0.020 |
=0.30 |
0.040 |
|
P265GH |
1.0425 |
=0.20 |
=0.40 |
=1.40 |
0.025 |
0.020 |
=0.30 |
=0.08 |
=0.30 |
=0.020 |
=0.30 |
0.040 |
|
16Mo3 |
1.5415 |
0.12-0.20 |
0.40-0.90 |
0.40-0.90 |
0.025 |
0.020 |
=0.30 |
0.25-0.35 |
=0.30 |
=0.040 |
=0.30 |
|
|
14MoV6-3 |
1.7715 |
0.10-0.15 |
0.15-0.35 |
0.40-0.70 |
0.025 |
0.020 |
0.30-0.60 |
0.40-0.50 |
=0.30 |
=0.040 |
=0.30 |
|
|
13CrMo4-5 |
1.7335 |
0.10-0.17 |
=0.15 |
0.40-0.70 |
0.025 |
0.020 |
0.70-1.15 |
0.40-0.60 |
=0.30 |
=0.040 |
=0.30 |
|
|
10CrMo9-10 |
1.7380 |
0.08-0.14 |
0.08-0.14 |
0.30-0.70 |
0.025 |
0.020 |
2.00-2.50 |
0.90-1.10 |
=0.30 |
=0.040 |
=0.30 |
|
|
25CrMo4 |
1.7218 |
0.22-0.29 |
0.22-0.29 |
0.60-0.90 |
0.025 |
0.020 |
0.90-1.20 |
0.15-0.30 |
=0.30 |
=0.040 |
=0.30 |
|
|
15NiCuMoNb5-6-4 |
1.6368 |
=0.17 |
=0.17 |
0.80-1.20 |
0.025 |
0.020 |
=0.30 |
0.25-0.50 |
1.00-1.30 |
=0.050 |
0.50-0.80 |
|
|
X10CrMoVNb9-1 |
1.4903 |
0.08-0.12 |
0.08-0.12 |
0.30-0.60 |
0.025 |
0.020 |
8.00-9.50 |
0.85-1.05 |
=0.40 |
=0.040 |
=0.30 |
|
|
a Ni chaniateir ychwanegu elfennau nas cynhwysir yn y Tabl hwn yn fwriadol at y dur heb gytundeb y prynwr, ac eithrio elfennau y gellir eu hychwanegu at orffen y cast. Rhaid cymryd pob cam priodol i atal ychwanegu elfennau annymunol o sgrap neu ddeunyddiau eraill a ddefnyddir yn y broses gwneud dur |
||||||||||||
|
b Nid yw'r gofyniad hwn yn berthnasol ar yr amod bod y dur yn cynnwys swm digonol o elfennau rhwymo nitrogen eraill y mae'n rhaid rhoi gwybod amdanynt. Wrth ddefnyddio titaniwm, bydd y cynhyrchydd yn gwirio bod (Al+Ti/2)=0,020% |
||||||||||||
|
c Opsiwn 2: Er mwyn hwyluso gweithrediadau ffurfio dilynol, bydd uchafswm cynnwys copr y cytunwyd arno yn is na'r hyn a nodir ac uchafswm cynnwys tun penodedig yn berthnasol. |
||||||||||||
|
d Nid oes angen adrodd ar gynnwys yr elfennau hyn oni bai eu bod yn cael eu hychwanegu'n fwriadol at y cast |
||||||||||||
|
e Ar gyfer trwch wal=30 mm gall y cynnwys carbon gael ei gynyddu 0.02% ar gyfer dadansoddi cast a chynnyrch |
||||||||||||
|
f Ni ddylid mynd y tu hwnt i'r gwerth carbon uchaf o 0,23% ar gyfer dadansoddi cynnyrch |
||||||||||||
EN 10216-2 Eiddo Mecanyddol
|
Gradd dur |
Priodweddau tynnol ar dymheredd ystafell |
Eiddo effaith ab |
|||||||||||
|
Enw dur |
Rhif Dur |
Cryfder cnwd uchaf neu gryfder prawf ReH neu Rp0.2 ar gyfer Trwch Wal T Isafswm. |
Tynnol Cryfder Rm |
Elongation Mae munud. % a |
Isafswm egni cyfartalog wedi'i amsugno KV J ar dymheredd gradd |
||||||||
|
T Llai na neu'n hafal i 16 |
160 |
40 |
60 |
l |
t |
l |
t |
||||||
|
MPa |
MPa |
MPa |
MPa |
MPa |
20 |
0 |
-10 |
20 |
0 |
||||
|
P195GH |
1.0348 |
195 |
320-440 |
27 |
25 |
40 c |
28 d |
27c |
|||||
|
P235GH |
1.0345 |
235 |
225 |
215 |
360-500 |
25 |
23 |
40 c |
28 d |
27c |
|||
|
P265GH |
1.0425 |
265 |
255 |
245 |
410-570 |
23 |
21 |
40 c |
2s d |
27C |
|||
|
16Mo3 |
1.5415 |
280 |
270 |
260 |
450-600 |
22 |
20 |
40 c |
27 c |
||||
|
14MoV6-3 |
1.7715 |
320 |
320 |
310 |
460-610 |
20 |
18 |
40 c f |
27 c |
||||
|
13CrMo4-5 |
1.7335 |
290 |
290 |
280 |
440-590 |
22 |
20 |
40 c |
27 c |
||||
|
10CrMo9-10 |
1.7380 |
280 |
280 |
270 |
480-630 |
22 |
20 |
40 c |
27 c |
||||
|
25CrMo4 |
1.7218 |
345 |
345 |
345 |
540-690 |
18 |
15 |
40 c f |
27 c |
||||
|
15NiCuMoNb5-6-4 |
1.6368 |
440 |
440 |
440 |
440e |
610-780 |
19 |
17 |
40 c f |
27 c |
|||
|
X10CrMoVNb9-1 |
1.4903 |
450 |
450 |
450 |
450 |
630-830 |
19 |
17 |
40 c f |
27 c |
|||
|
a I=hydredol t=traws |
|||||||||||||
|
b I'w ddilysu pan nodir opsiynau 4 a/neu 5, oni bai bod troednodyn f) yn berthnasol |
|||||||||||||
|
c Opsiwn 4: Bydd ynni effaith yn cael ei wirio. |
|||||||||||||
|
d Opsiwn 5: Bydd ynni effaith hydredol yn cael ei wirio. |
|||||||||||||
|
e Ar gyfer trwch wal 60 mm< T =80mm |
|||||||||||||
|
f Prawf effaith yn orfodol ar gyfer trwch wal T =16mm |
|||||||||||||
EN 10216-2 Triniaeth Gwres tiwb boeler
|
Gradd dur |
Triniaeth wres a |
Austenizing |
tymheru |
|||
|
Enw dur |
Rhif dur |
Gradd tymheredd |
Oeri Canolig |
Gradd tymheredd |
Cyfrwng oeri |
|
|
P195GH |
1.0348 |
+N b |
880 i 940 |
Awyr |
- |
- |
|
P235GH |
1.0345 |
+N b |
880 i 940 |
Awyr |
- |
- |
|
P265GH |
1.0425 |
+N b |
880 i 940 |
Awyr |
- |
- |
|
16Mo3 |
1.5415 |
+N b |
890 i 950 |
Awyr |
- |
- |
|
14MoV6-3 |
1.7715 |
+NT bc |
930 i 990 |
Awyr |
680 i 730 |
awyr |
|
13CrMo4-5 |
1.7335 |
+NT bc |
900 i 960 |
Awyr |
660 i 730 |
awyr |
|
10CrMo9-10 |
1.738 |
+NT bc |
900 i 960 |
Awyr |
680 i 750 |
awyr |
|
25CrMo4 |
1.7218 |
+QT |
860 i 900 |
Aer neu Hylif |
620 i 680 |
awyr |
|
15NiCuMoNb5-6-4 |
1.6368 |
+NT c |
880 i 980 |
Awyr |
580 i 680 |
awyr |
|
X10CrMoVNb9-1 |
1.4903 |
+NT c |
1040 i 1090 |
awyr |
730 i 780 |
awyr |
|
a +N=Normaleiddio, +NT=Normaleiddio + Tempering, +QT=Quenching + Tempering (aer neu hylif), +I=Anelio Isothermal. |
||||||
|
b Mae normaleiddio yn cynnwys Normaleiddio Ffurfio. |
||||||
|
c For these steel grades it may be necessary in the case of wall thickness T above 25 mm or T/D >0,15 i gymhwyso diffodd a thymheru er mwyn cyflawni'r strwythur a'r priodweddau materol a fwriedir. Bydd y penderfyniad yn cael ei adael i ddisgresiwn y gwneuthurwr ond caiff ei ddatgan i'r cwsmer ar adeg yr ymholiad a'r archeb. Rhaid i diwbiau dur sy'n cael eu trin yn y fath fodd gael eu dynodi gan yr enw dur wedi'i ategu gan y symbol + QT. |
||||||